Using Fumed Alumina To Fix Paper Issues in Van Dyke Brown


An Easy & Cost Effective Way To Fix Paper Issues!

Stormy Seas, Van Dyke Brown, Lana Paper, Fumed Alumina Brush Coated, Gold Toned

Stormy Seas, Van Dyke Brown, Lana Paper, Fumed Alumina Brush Coated, Gold Toned, 720nm Infrared

Testing Fumed Alumina…

Van Dyke Brown emulsion is basically on the acidic side of things chemically and as a result of this I have been forced to wash most of my papers with a acid bath. This caused a increase in my process by 2 days. So I am testing Fumed Alumina which is acidic unlike Fumed Silica which is neutral. I decided to go with the Alumina test first and will do a followup post down the line with the Fumed Silica.

Bent Tree, Van Dyke Brown, Lana Paper, Fumed Alumina Brush Coated, Gold Toned

Bent Tree, Van Dyke Brown, Lana Paper, Fumed Alumina Brush Coated, Gold Toned, IR400 120 Film

Initial results were quite pleasing with both Revere Platinum and Lana Aquarelle papers. I got a MAJOR increase in Dmax with both the Lana and Revere papers, but upon completion of my final wash the Revere was VERY EASY to damage with finger smudges until it dried. The Revere had a tendency for the Alumina to easily rub off the Alumina while wet whereas the Lana was strongly attached.

Anderson Mill, Van Dyke Brown, Lana Paper, Fumed Alumina Brush Coated, Gold Toned

Anderson Mill, Van Dyke Brown, Lana Paper, Fumed Alumina Brush Coated, Gold Toned, Leica M Monochrom

The Alumina did fix ALL of the spotting issues that I had when using the Revere Platinum paper but the fact that it will rub off when wet causes some concern but it is easily overcome with careful handling.

Magnolia, Van Dyke Brown, Lana Paper, Fumed Alumina Brush Coated, Gold Toned

Magnolia, Van Dyke Brown, Lana Paper, Fumed Alumina Brush Coated, Gold Toned

The Process:

  1. Dry roll on the Fumed Alumina in 2 directions and rap the paper edge on the table to remove the excess.  Make sure that you use a good mask to filter out this dust as it might irritate your lungs.  DO NOT OVER COAT or you will get streaks when you coat the emulsion.  The rolling step only takes about 30 seconds! You will need to put about 1 TSP of the Alumina into a small paint tray then pre load a small (3″) HARD foam roller with it.
  2. Coat as normal after you roll on the Alumina. You will need about 12 extra drops of VDB emulsion due to it absorbing more. My basic quantity of VDB emulsion for a 8×12 sheet of paper coated with Alumina is 48 Drops of emulsion and 2 drops of Tween 20 at 25% (you will need to dilute the Tween from 50%) solution.  For this post I brushed on the emulsion.  In the past I would normally use a glass rod for coating but the Alumina creates a very rough surface and I was afraid of damaging the paper.
  3. Dry and Expose. Here you will find that the addition of the Alumina will DECREASE your exposure about 1.5 stops!
  4. 1st water bath with distilled water and a pinch of citric acid, 2 min.  This bath will remove any extra ferric ammonium citrate which will cause a yellow paper stain. This bath will darken the print.  Do not worry as the FIX will balance contrasts and bring out the highlights!
  5. Fresh water bath to remove citric acid. 2 min. If you are Gold Toning, this step is VERY important as any Citric Acid will destroy the toner bath!  
  6.  Gold toning bath 2 to 5 min to taste.  The toning process requires CONSTANT AGITATION! After 2 or 3 prints toned add 5ml/print of Gold Chloride to bring the bath back up to strength. This  toning bath will further darken the print.  Do not worry as the FIX will balance contrasts and bring out the highlights!
  7. Fix for 2 min with Sodium Thiosulfate for 2 min. 30g/L. I do not believe that any further time will help the process.
  8. Final moving fresh water bath for 30 min.
  9. Air dry,  I spread out old towels on a table top and place the print on it for about 10 min to absorb most of the water thru the back of the print.  I will then hang the prints to dry by a corner.  
  10. Use a  heat press to flatten your prints at 170deg for 20 seconds. The heat press step is to make the paper flat again.
  11. Hand rub in SOFT custom wax coating for protection then heat to force the wax to be absorbed into the paper fiber with a hair drier (more about this in a future post).
Dinghy, Van Dyke Brown, Lana Paper, Fumed Alumina Brush Coated, Gold Toned

Dinghy, Van Dyke Brown, Lana Paper, Fumed Alumina Brush Coated, Gold Toned, Leica M Monochrom

All in all this was a VERY easy fix to the acid washing step  and only added about 30 seconds to roll on the Alumina. The Fumed Alumina can be purchased at Bostick & Sullivan for $15/500g which will do about 100 sheets of 8×12 paper.

2 Dinghys, Van Dyke Brown, Lana Paper, Fumed Alumina Brush Coated, Gold Toned

2 Dinghys, Van Dyke Brown, Lana Paper, Fumed Alumina Brush Coated, Gold Toned, Leica M Monochrom

The increase in Dmax with the Fumed Alumina is amazing and the resulting images are stunning.

Please let me know what you think of this post and with suggestions for future posts!

Advertisements

Going Home to Momma with the Leica M7…. Film Photography Returns!


Ahhh… It Feels So Good!

Rollei IR400 Film - Leica M7 50mm Lux - Rodinal 1-50

Spring in the South…  Rollei IR400 Film – Leica M7 50mm Lux – Rodinal 1-50

Oh my, I do NOT know where it came from but I got the BUG again for more film photography!  I have a cabinet here in the Gallery just full of old film cameras plus a Leica M7 film body that works with ALL OF MY M MOUNT LENSES!  (see the last post HERE for more info on the lenses).  I decided to purchase a new stock of several films:

  • Kodak Tri-X 400, Ohh
  • Eastman Double X 200, Ahh
  • Rollei IR400  400, WOW!
  • Kodak Tmax, Ho hum…
  • Ilford HP5+ 400
Rodinal One Shot

Rodinal One Shot

I picked up some stainless 2 roll developing tanks with a bunch of Hewes (don’t skimp on your reels, buy the best!) Stainless Steel 35mm Reels.  For developing I like Rodinal One Shot due to its ease of use and a life span of around 40 years.  I simply mix it one tank at a time usually at a 1:50 ratio with water using a small syringe. It allows a very wide latitude of contrast and iso control.  I have used several other developers but I keep coming back to Rodinal!

Now, I am playing with several cameras. As I said my main and BEST camera is my Leica M7.  But here is a current list of those cameras I am using:

  • Leica M7 with Leica & Voigtlander Lenses
  • Petri 7s, 1962 
  • Olympus XA
  • Olympus 35 RC 
  • Shen Hao 4×5 Field Camera (about 12 years old)
1962 Custom Petri 7s Film Body

1962 Custom Petri 7s Film Body

The Petri 7S has been in my hands since 1962 and still shoots great ( I did send it off to have the light seals replaced and a new leather covering ). The Petri has no batteries but rather a solar cell around the lens that drives a needle exposure meter that you simply place into its center notch for a good image!

All of the cameras in my list above have proven reliable  but with the Petri you get a link to the past, specifically MY past as this was my 2nd camera I owed when I was young!

The Olympus 35 RC is an amazing small rangefinder with very nice controls.  It is smaller then the Petri 7s and actually has better control functionality.  It does require a battery to run its metering system though which is a step down from the Petri 7S in my opinion.  The nice thing other than the size is the fact that EVERYTHING is displayed inside of the viewfinder.   Unlike a refurbished Petri 7S which can be found for around $100 used on Ebay, the Olympus 35 RC camera refurbished is demanding around $250!  This is a big difference in price and tells you a lot about its quality and demand! I was lucky to find one from a collectors inventory that he sent off to be totally refurbished and re-skinned for much less than $200.00!  For you film shooters out there on a budget this is the camera that I recommend if you find yourself desiring a rangefinder.

My Custom Olympus 35 RC

My Custom Olympus 35 RC

The Olympus XA was a 35mm rangefinder camera built by Olympus of Japan. It was one of the smallest rangefinder cameras ever made, together with the Contax T.

Olympus-XA

Olympus-XA

It was designed by Yoshihisa Maitani who had joined Olympus Optical Co Ltd in 1956. He was the chief camera designer and managing director of Olympus Optical Co Ltd., having developed a number of legendary cameras during his career. These included the Pen series, the OM series, the XA series, the IS series and the [mju:] series of cameras.

The original model, the XA, was sold from 1979 to 1985. The original XA features true rangefinder focusing, a fast 35mm f/2.8 lens, and aperture prioritymetering. The lens was protected by a sliding dust cover.

This is the smallest 35mm rangefinder ever made.  It will fit in the palm of my hand and will make a great system to have with me everywhere I go!

The Leica M7 uses batteries and sports a center weighted spot meter measured either off the film or off the shutter.  I find that it meters very reliable. It is the top of the heap when it comes to 35mm film cameras.  There are a lot of high end rangefinder cameras on the market but the Leica is the top.  I really excels in the area of long exposures with either a count down timer  in the viewfinder for images metered and controlled in the aperture priority mode or a count up timer for exposures done in the bulb mode.  In bulb, it will count up to 16 min then stops counting for battery conservation, but will continue exposing until you release the remote shutter release.  It will use NO battery power after the 16 min count up timer turns off until you release the shutter then it requires a pulse of electricity to close the shutter.   NO other rangefinder can say this unless you use a pure mechanical camera like a Leica M2 which has no metering system at all.

The Leica M7 is surprisingly heavy but easy to handle.  I keep reading about other high end rangefinder bodies out there but when you do the comparison of features I always come back to the M7.

My Leica M7 Film Body

My Leica M7 Film Body

All of my cameras are fun to use and reliable.  With the Leica M7 you get the world class glass but with the Petri 7S you get a link to the past, specifically MY past as this was my 2nd camera I owed when I was young!  The Olympus 35 RC is an advanced rangefinder from the 1970 era and is slick and fun to shoot. You will see examples from these cameras towards the end of this post!

______________________________________________________

I usually develop my negatives on Sundays.  I have a film drying cabinet that I use to dry the film without dust spots overnight.  I then will scan the negatives on Monday or Tuesday using a Nikon 4000 ED film scanner at 4000 dpi into the DNG format for editing and cleaning later in the week.  I usually shoot 2 or 3 rolls a week.

Rollei IR400 Film

Rollei IR400 Film

My favorite film is Rollei IR400.  This is available at the big camera stores like Digitaltruth, Freestyle and B&H.  What makes this film so special is the fact that is very much like Kodak Tri-X 400 as shot.  It has a VERY THIN film base which really makes scanning easy.  BUT the most amazing thing about this film is that it is sensitive to INFRARED!  If you place a Hoya R72 IR filter on the camera lens the film will record 720nm IR images!  There is an ISO hit due to the filter being so dark down to 12 ISO but it is worth it being able to shoot in both normal B&W and IR B&W!

Next I like the Kodak Tri-X 400 film.  It gives great contrasts and has a very wide latitude in development.  It is well known and tested and for ultra long exposures.

Eastman Double X 5222

Eastman Double X 5222

Then comes Eastman Double X Cinema film.  This is a GREAT B&W film that gives a very smooth gradation and lovely warm tonality with slightly increased contrasts.  This is motion picture film so unless you are going to buy a 400 foot reel you will need to purchase it from the store at Film Photography Project. They will sell it in either 24 exposure rolls or a 100 foot bulk loader roll.  It develops nicely in Rodinal at 1:60 for ISO 200 but there are ratios for 100 up to 800 ISO!  This film is very much worth experimenting with.

I need to say a few words about the folks at Film Photography Project.  They offer  an amazing wide selection of films and old cameras!  This includes Polaroid cameras and film also!  Their Podcast is amazing and I find that it is so good that I now have it running all day while I am working at my gallery in Pawleys Island.  Good Stuff, check them out here:  Film Photography Project.

Whatever film you decide to use you will be pleased with the results. Processing is easy to do with a VERY small investment. You will need:

  • Film Camera
  • Film
  • Chemestry:  Developer, Stop (you can use water), Fixer and water bath with a Wetting Agent.  $40 to get started
  • Film drying hanger clips $3 for a bag of 2
  • Film tank, either stainless steel or a Peterson. Peterson tank and reel is about $40
  • Film tank reels (if stainless do not skimp on these).  Hewes Steel are about $25 each
  • Dark changing bag to move the film from the canister to the developing tank.   $40
  • You will also need some way to scan your film into a digital image or pay someone to do it for you.

That is it.  It normally takes me about an hour to develop 2 rolls.  I will let them dry for several hours then cut them into strips of 6 and put them into plastic storage sheets.

For scanning, as I said above, I use a Nikon 4000ED film scanner.  As you can guess from the name it will scan at 4000 dpi and has a lot of adapters for different types of film scan feeders.  It has slide auto feeders, single slide feeders, a 6 position film rail for troublesome film and an automatic roll feeder to scan entire rolls automatically.  If you couple this with VIEWSCAN software you have an amazing scanning system that rivals those that pro labs use!

Nikon 4000 ED system

Nikon 4000 ED system

Ok, lets take a look at the results of 3 types of film in 2 cameras!

Pawleys Pier  M7 Elmarit 28  Rollei IR400 film in Rodinal at 1:50

Pawleys Pier M7 Elmarit 28 Rollei IR400 film in Rodinal at 1:50 240 second exposure

1962 Petri 7S, Eastman Double X film in Rodinal at 1:60

1962 Petri 7S, Eastman Double X film in Rodinal at 1:60

Eastman Double X Film - 1962 Petri 7S  - Rodinal 1-50

Eastman Double X Film – 1962 Petri 7S – Rodinal 1-50

1962 Petri 7S, Eastman Double X film in Rodinal at 1:60

1962 Petri 7S, Eastman Double X film in Rodinal at 1:60

1962 Petri 7S, Eastman Double X film in Rodinal at 1:60

1962 Petri 7S, Eastman Double X film in Rodinal at 1:60

1962 Petri 7S, Eastman Double X film in Rodinal at 1:60

1962 Petri 7S, Eastman Double X film in Rodinal at 1:60

Rollei IR400 Film - Leica M7 50mm Lux - Rodinal 1-50

Rollei IR400 Film – Leica M7 50mm Lux – Rodinal 1-50

Rollei IR400 Film - M7 28mm Elmarit - Rodinal 1-50

Rollei IR400 Film – M7 28mm Elmarit – Rodinal 1-50

Rollei IR400 Film - M7 50mm Lux - Rodinal 1-50 240 second exposure

Rollei IR400 Film – M7 50mm Lux – Rodinal 1-50 240 second exposure

Rollei IR400 Film with R72 IR Filter - M7 50mm Lux - Rodinal 1-50

Rollei IR400 Film with R72 IR Filter – M7 50mm Lux – Rodinal 1-50

 

Rollei IR400 Film - M7 50mm Lux - Rodinal 1-50

Rollei IR400 Film – M7 50mm Lux – Rodinal 1-50

I hope that you enjoyed this post and its associated images.  I have been using film since I was 9 years old.  At 13 I had my first darkroom at home.  I worked in film in my own darkroom until I was 18 when that period of my life can to an end.  42 years later I re-engaged film photography again and cannot help but ask “Why did I wait so long?”  I have been shooting digital since my career at Eastman Kodak when you could ONLY get B&W digital camera systems!  I have spent fortunes on digital and have loved every moment of it.  Film will NOT take any of that away, I still have digital and continue to use it.  But I have to be honest and admit that working in film again fills me with a sense of peace that I have not experiences in a very long time….

Please let me know what you think of this post!

Using the Fuji X Pro 1 for Pinhole Photography!


All of this Perfection and Pinhole too!?!

Pinhole

Oh boy!  I do so love the use and functionality of the new Fuji X Pro 1 camera system!  I have it plus the Fuji system lenses (35mm, 18mm & the 60mm) and haven’t touched my other camera systems since it arrived!   But, the point of this post is Pinhole Photography!  Last Sunday was the World Wide Pinhole day.  This got me thinking earlier in the month that I ought to be able to use the X Pro 1 for this as well.  No one makes a pinhole plate for the Fuji X mount lens system as of yet, so what to do?  Well, I had purchased the  Kipon Leica M converter for the X Pro 1 in advance of getting the Voigtlander Super Wide Heliar 15mm f/4.5 M  lens and thought: “Why don’t I find a pinhole plate to fit the Leica M?”

Skink Pinhole Plate For Leico M

Well, sure enough there it was on EBay!  Skink out of Germany and they had several models and one of them caught my eye.  It is 24mm wide and has a aperture of f/110.  It is all black and came with the pinhole, a zone plate and a sieve plate!  So I ordered it and had it arrive before the pinhole day.   I did some initial testing and found that if you select the 24mm frame lines that it matches up perfectly with the pinhole plate with the optical viewfinder!  What more could you ask for? Of course with any pinhole work you are required to work on a tripod and this is no exception.  The nice thing about using the X Pro 1 for pinhole is that the gain of the LCD view changes dynamically and allows you to see the image on the back of the camera for setup and composition!  There is no focus of course so it is just basically point and shoot from the tripod.

I have always been passionate about the old ways in photography.  I still have film in my freezer and a 4×5 film camera in a glass case waiting for the day to be used again! But I also have various pinhole systems in film and adapter plates for ALL of my digital camera systems.  I have purchased several from Linex Laser and many from Skink, I even have the Pinwide adapter for micro 4/3’s.  The point is, that shooting with pinholes is just plain fun.  People walk by and always ask what I am doing since they see no lens.  If you have not tried this old technology you should give it a try. It is inexpensive (well except for the X Pro 1 since you also have to have an adapter) and will amaze you with the results!

Now, REMEMBER, pinhole photography does NOT use a lens of any type!  It uses a simple hole in a metal plate thru which the light passes and diffracts!  The resulting image on the film or sensor is slightly diffused but equally sharp from the lens to infinity!  All of this with no glass lens!

Well suffice it to say, Pinhole day was a great success and filled with fun!  If you have not tried it you really should.  You do not have to purchase a pinhole, you can modify your camera body cap and create one yourself, it is very easy!

Here are some images for you to consider.  Most are taken with the X Pro 1 but one or two are on a Micro 4/3 body only to show that ANY camera system will do for this!

Pawleys Marsh Pinhole. X Pro 1

Pawleys Island Marsh Pinhole, X Pro 1

Fuga City Detail Pinhole, GH2

Pin Hole Photography Primer…


Today is the day!  Get out your Pin Hole cameras and go shooting!

World Wide Pinhole Photography Day, 2012!

Fuga City Detail, Pinhole image, Panasonic GH2 with the PinWide f/127 pinhole plate.

Today is the world wide pinhole photography day.  Thousands of folks around the world are out shooting pinhole images today and posting them on the http://www.pinholeday.org/ web site.  It is great fun and takes us back to an era when photographic experimentation was the word of the day!  A pinhole camera system is one without a lens. I simply has a VERY SMALL hole thru which the light passes and creates the image on the back of the camera on film or sensor.  You can purchase pinhole plates for most cameras made today plus you can easily create one of your own!

Do a little research here on the net thru Google and you will find a ton of information on it.  But remember today is the yearly big day!

I have pinhole plate adapters for ALL OF MY CAMERA systems.  There are many companies who make them.  Here is a short list to get you started:

  • Skink (ebay) (For ALL cameras)
  • Pinwide (for Micro 4/3)
  • Lenox Laser (good selection of models for various cameras!
  • Lens Baby

Here are what some of these plates look like…

Pinhole images are typically not very sharp, BUT they are at the same sharpness from the very front edge of the pinhole plate to infinity!  They can be created with one to several pinholes and there is no limit to how the film can be placed, flat, curved, round and so on!  For digital systems, you can indeed have multiple pinholes, but only a flat sensor.  They can and will create very etherial images that are very pleasing to the eye and great fun to create!

Here are some example images of my own pinhole creations, please let me know what you think!!

Pawleys Marsh Pinhole image. Leica M mount Skink f/207 pinhole plate at 3.2 second exposure

Pawleys Marsh Pinhole image. Leica M mount Skink f/207 pinhole plate at 3.2 second exposure

Fuga City Detail, Pinhole image with the Pin Wide f/127 pinhole plate.

Fuga City Detail, Pinhole image with the Pin Wide f/127 pinhole plate.